Analisis Kekuatan Sambungan Las Butt joint pada Struktur Logam Baja A36 Menggunakan Simulasi SolidWorks
Keywords:
weld joint, ASTM A36, solidworks, tensile test, bending test, FEMAbstract
This research evaluates the mechanical strength of butt joint welds on ASTM A36 steel by comparing outcomes from laboratory testing and numerical simulations using SolidWorks. Physical experiments consisted of tensile and bending tests, while the simulation utilized the Finite Element Method (FEM). The tensile test produced an ultimate tensile strength of 498.4 MPa and a yield strength of 361.4 MPa, whereas the simulation yielded 475 MPa and 250 MPa, respectively. The bending test results indicated that the welded specimens exhibited good ductility without visible surface flaws. Differences between simulation and experimental data were mainly due to the idealized material properties in the software compared to the variability found in real specimens. These findings suggest that SolidWorks-based FEM simulation can serve as an effective preliminary tool for predicting weld joint performance, but physical testing remains necessary to validate and ensure reliability..
References
Arif, J., Prayitno, P., Al Hafidh, H., 2023. Analisis statik pada aluminium 5052 dengan variasi sudut menggunakan SolidWorks. TEKNOSAINS: Jurnal Sains, Teknologi dan Informatika, 10 (1), pp.38–50.
Arifin, J., Purwanto, H., Syafa, I., 2017. Pengaruh jenis elektroda terhadap sifat mekanik hasil pengelasan SMAW baja ASTM A36. Majalah Ilmiah Momentum, 13(1), pp.27-31
Bintarto, R., Widodo, T.D., Raharjo, R., Ma, M.S., Dewi, F.G.U., Pratama, G.D., 2020. Analisis struktur mikro dan kekuatan bending sambungan las TIG dengan perbedaan kuat arus listrik pada logam tak sejenis aluminium paduan 5052–baja galvanis dengan filler Al-Si 4043. Jurnal Rekayasa Mesin, 11 (1), pp.125–131.
Fazadima, A., Pratikno, H., Fazadima, H.I., 2022. Analisis pengaruh variasi heat input terhadap sifat mekanik dan laju korosi pada pengelasan SMAW sambungan pelat baja A36 dengan baja structural steel 400 (SS400). JURNAL TEKNIK ITS, 11(3), pp.38-43.
Gita, I.W.E.M.K., Darmadi, D.B., 2024. Pengaruh perlakuan PWHT pada baja ASTM A36 terhadap kekuatan tarik. Prosiding Seminar Nasional Terapan Riset Inovatif (SENTRINOV), 10 (1), pp.331–337.
Junaidi, A.K., Isra, A., Pertiwi, E., 2025. Sifat mekanik sambungan las butt joint pada plat ASTM A36 menggunakan las GTAW. SAINSTEK, 13 (1), pp.29–33.
Ma’arif, S., 2020. Distribusi tegangan pada sambungan las dissimilar antara ASTM A36 steel dan AISI 304 dengan SolidWorks. In: SERINA UNTAR 2020, Akselerasi Penelitian dan Pengabdian kepada Masyarakat untuk Pemberdayaan Masyarakat Indonesia. Jakarta, 2 Desember 2020.
Nugroho, A., 2018. Pengaruh variasi kuat arus pengelasan terhadap kekuatan tarik dan kekerasan sambungan las plate carbon steel ASTM 36. Jurnal Rekayasa Sistem Industri, 3 (2), pp.134–142.
Suwasono, B., Farizal, M., Nugroho, N.Y., Hardianto, D., 2023. Identifikasi kekuatan butt joint dan lap joint pada pengelasan konstruksi kapal. Rekayasa, 16 (2), pp.243–249.
Weldri, F., 2022. Analisis kekuatan sambungan las pada rangka mesin perontok padi multiguna. Strata 1. Universitas Muhammadiyah Sumatera Barat.